Si<sub>3</sub>N<sub>4</sub>/NS315合金高温微动磨损特性研究

李根; 刘捍卫; 任平弟; 张晓宇

Si₃N₄/NS315合金高温微动磨损特性研究

1. 西南交通大学材料先进技术教育部重点实验室, 成都, 610031;
2. 西南交通大学生命科学与工程学院, 成都, 610031

基金项目:

国家自然科学基金(51075342)

详细信息

作者简介:
李根(1986—),男,2012年毕业于西南交通大学机械学院机械设计制造及其自动化专业,获硕士学位。现主要从事微动磨损研究。刘捍卫(1955—),男,副教授,博士研究生。1992年毕业于西南交通大学金属材料及热处理专业,获硕士学位。现主要从事表面工程及摩擦学研究。任平弟(1960—),男,教授,博士。2005年毕业于西南交通大学机械设计及理论专业,获工学博士学位。现主要从事金属材料腐蚀磨损与防护的研究。

中图分类号: TG115.5⁺8
计量
- 文章访问数: 13
- HTML全文浏览量: 4
- PDF下载量: 0
- 被引次数: 0
出版历程
- 收稿日期: 2012-03-16
- 修回日期: 2012-10-20
- 网络出版日期: 2025-03-08

Study on Fretting Characteristics of Si₃N₄/NS315 Alloy at High Temperature

1. Key Laboratory of Advanced Technologies of Materials, Ministry of Education of China, Southwest Jiaotong University, Chengdu, 610031, China;
2. School of Life Science and Engineering, Southwest Jiaotong University, Chengdu, 610031, China

摘要

摘要: 使用液压式高精度微动磨损试验机PLINT,以陶瓷球Si₃N₄为对磨副对国产690合金(国内牌号NS315)进行室温以及高温条件下的微动磨损试验,分析其三维摩擦特性曲线、摩擦系数、磨痕形貌,探究其磨损机理。实验结果表明:当位移为80～200μm时,NS315合金处于滑移区;位移幅值对NS315合金的摩擦系数影响较小;法向载荷增加时,NS315合金摩擦系数升高;与室温相比,高温条件下NS315合金摩擦系数较高、磨损量较大,磨损情况严重;室温时,NS315合金磨损机理主要为磨粒磨损,而高温300℃时,其磨损机理主要表现为摩擦氧化以及剥层。
- 690合金 /
- 微动磨损 /
- 核电设备 /
- 高温
Abstract: The fretting wear behaviors of NS315 alloy were studied experimentally on a high precision hydraulic fretting wear machine at room temperature（25℃） and 300℃.This paper was designed to analyze the the friction characteristic curve,the fretting coefficients and the morphology of the worn surface,and the mechanism of fretting wear was discussed.Experimental results shows that the fretting wear of NS315 alloy is in a slip regime when the displacements are 80~200 μm.Friction Coefficient was not significantly related to the displacements but increased according to the normal load’s increment.Compared to the room temperature,NS315 Alloy got a higher friction coefficients,and the worn volume was larger at 300℃.The wear mechanism of the NS315 Alloy at 25℃ were mainly a combination of abrasive wear,delamination and oxidization wear,yet oxidization wear and delamination at 300℃.
- NS315 alloy /
- Fretting wear /
- Nuclear power equipment /
- High temperature