YAN Meng, PENG Qian, ZHAO Wenjin, SHENG Zhongqi, DAI Xun. Fracture Morphology Analysis of Iodine Induced Stress Corrosion Cracking of N36 Zirconium Tube[J]. Nuclear Power Engineering, 2012, 33(S2): 47-50.
Citation: YAN Meng, PENG Qian, ZHAO Wenjin, SHENG Zhongqi, DAI Xun. Fracture Morphology Analysis of Iodine Induced Stress Corrosion Cracking of N36 Zirconium Tube[J]. Nuclear Power Engineering, 2012, 33(S2): 47-50.

Fracture Morphology Analysis of Iodine Induced Stress Corrosion Cracking of N36 Zirconium Tube

  • Received Date: 2012-10-14
  • Rev Recd Date: 2012-12-08
  • Available Online: 2025-03-08
  • Hoop tensile test is performed on N36 zirconium tube ring specimen at 350℃ iodine gas en-vironment to study the I-SCC behavior of N36 zirconium tube under iodine action.The fracture surface after I-SCC is observed by scanning electron microscope,and the result shows that pitting is prone to take place at edge of specimen,and group of cracks propagate parallel to the fracture surface.There is no clear boundary between intergranular and transgranular crack.

     

  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Article Metrics

    Article views (19) PDF downloads(0) Cited by()
    Proportional views
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return