Effect of Sn Content on Corrosion Resistance of Zr-Sn-Nb Alloys in Steam

  • Received Date: 2012-10-25
  • Rev Recd Date: 2012-11-25
  • Available Online: 2025-03-08
  • The corrosion behaviors of Zr-xSn-1Nb-0.3Fe(x=0~1.5wt%) alloys have been investigated in the superheated steam of 400℃/10.3 MPa for 270 days.Results show that the corrosion weight distinctly de-creased with the decreasing of Sn content from 1.5wt% to 0.8wt%.However,the corrosion weight was hardly changed when the Sn content was 0 0.8wt%.The characteristics of grains and second phase particles were analyzed by optical microscope(OM) and scanning electron microscope(SEM),respectively,and the crystal structure of oxide films formed on specimens after corrosion test were characterized by X-ray diffraction(XRD) method.The microstructural characteristics indicated that some Sn promoted the recrystallization of Zr-1Nb-0.3Fe alloy,and the area fraction of precipitates in the alloy was increased with the Sn content de-creased when all the samples were the same heat treatment condition.It was found that,the higher the fraction of the tetragonal ZrO2 in the oxide films was,the lower the corrosion rate of specimens,and it can be con-cluded that the tetragonal ZrO2 in the oxide films makes for the corrosion resistance.

     

  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Article Metrics

    Article views (20) PDF downloads(0) Cited by()
    Proportional views
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return