Ti-Al-Zr合金的氢致脆性研究

刘彦章; 黄新泉; 邱绍宇; 祖小涛; 康鹏

Ti-Al-Zr合金的氢致脆性研究

1. 中国核动力研究设计院核燃料及材料国家级重点实验室, 成都, 610041;
2. 电子科技大学应用物理系, 成都, 610054;
3. 西华大学材料科学与工程系, 成都, 610039

详细信息

作者简介:
刘彦章(1975—),男,博士研究生。2000年毕业于四川大学固体物理及技术专业。现从事材料结构与性能研究。

黄新泉(1957—),男,研究员。1983毕业于哈尔滨船舶学院材料专业。现从事反应堆结构材料研究。

邱绍宇(1964—),男,研究员。核燃料与材料国家重点实验室常务副主任。1984年毕业于重庆大学金属材料专业。现从事反应堆结构材料研究。

中图分类号: TL341
计量
- 文章访问数: 6
- HTML全文浏览量: 2
- PDF下载量: 0
- 被引次数: 0
出版历程
- 收稿日期: 2004-03-04
- 修回日期: 2004-10-18
- 网络出版日期: 2025-07-31
- 刊出日期: 2005-10-15

Study of Hydrogen Induced Embrittlement of Ti-Al-Zr Alloys

1. National Key Laboratory. for Nuclear Fuel and Materials, Nuclear Power Institute of China, Chengdu, 610041, China;
2. Department of Applied Physics, University of Electronic Science and Technology, Chengdu, 610054, China;
3. Department of Material Science and Engineering, Xihua University, Chengdu, 610039, China

摘要

摘要: 为了研究氢进入钛合金试样后对其力学性能的影响,探索氢在钛合金中的行为,本文用电解渗氢方法对Ti-Al-Zr合金进行了渗氢处理,得到了不同含氢量的试样。在室温下进行了试样的拉伸、冲击实验。结果表明,试样渗氢后的强度得到不同程度的提高,这是固溶强化的结果;试样的塑性随氢含量的提高而下降,当氢含量达到~1200μg/g时,塑性损失达到25%;试样的冲击韧性随氢含量的提高而下降,试样中氢含量达到~300μg/g时,冲击韧性下降~80%,试样已基本上呈脆性。使用SEM研究了渗氢样品的断口形貌后发现,拉伸试样中只有少量二次裂纹,而冲击试样有大量二次裂纹产生,并伴有准解理特征。
- Ti-Al-Zr合金 /
- 电解渗氢 /
- 氢脆 /
- SEM
Abstract: The tensile and impact tests of the cathodic charging Ti-Al-Zr alloy were measured with the hydrogen concentration up to 1200 μg/g in order to study the behavior of hydrogen in titanium alloys.The results showed that the strength of the alloy had increased and this was the result of solid solution strengthen-ing.The total elongation exhibited a negative dependence on the hydrogen and decreased with the hydrogen monotonically from ~30% to 22% in the range.The absorbed energy also exhibited a negative dependence on the hydrogen and decreased by 80% at ~300 μg/g,which reflected that this alloy had much sensitivity to em-brittlement by hydrogen even in the slight increase of hydrogen content.The fracture characteristics for the tensile and impact specimens were analyzed,and it showed that there existed a lot of large secondary cracks in the impact specimens,and the fracture mode was changed from ductile to cleavage as the hydrogen content increases.However,there only had some small secondary cracks in the tensile specimens.
- Ti-Al-Zr alloy /
- Cathodic charging /
- Hydrogen embrittlement /
- Scanning electron microscope（SEM）