ZU Xiao-tao, FENG Xiang-dong, DENG Jiong, QIU Shao-yu, ZHOU Ji-meng, WANG Zhi-guo. Surface Modification of a Ti-2AI-2.5Zr Alloy by N Ion Implantation[J]. Nuclear Power Engineering, 2004, 25(3): 233-235,251.
Citation: ZU Xiao-tao, FENG Xiang-dong, DENG Jiong, QIU Shao-yu, ZHOU Ji-meng, WANG Zhi-guo. Surface Modification of a Ti-2AI-2.5Zr Alloy by N Ion Implantation[J]. Nuclear Power Engineering, 2004, 25(3): 233-235,251.

Surface Modification of a Ti-2AI-2.5Zr Alloy by N Ion Implantation

  • Received Date: 2002-12-15
  • Rev Recd Date: 2003-11-17
  • Available Online: 2025-07-28
  • Publish Date: 2004-06-01
  • Implantation-enhanced hardening of a Ti-2Al-2.5Zr alloy by 75keV nitrogen ion implantation with the dose of 3×1017 N+ cm-2 and 8×1017 N+ cm-2 is investigated. The surface characterization of samples was studied by XRD and Vickers hardness tests. The nitrogen implantation increases the surface hardness up 340% and 260 for the dose of 8×1017 and 3×1017 N+ cm-2, respectively. The results of XRD analysis show that TiN is formed in the surface region. Nitrogen-ion-implantation-enhanced hardening is mainly due to the formation of TiN.

     

  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Article Metrics

    Article views (8) PDF downloads(0) Cited by()
    Proportional views
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return