TANG Rui, WANG Ji-ping, LONG Chong-sheng, JIN Zhi-hao. Structure and Properties of C/C-SiC Prepared by Reactive Melt Infiltration[J]. Nuclear Power Engineering, 2009, 30(1): 68-73.
Citation: TANG Rui, WANG Ji-ping, LONG Chong-sheng, JIN Zhi-hao. Structure and Properties of C/C-SiC Prepared by Reactive Melt Infiltration[J]. Nuclear Power Engineering, 2009, 30(1): 68-73.

Structure and Properties of C/C-SiC Prepared by Reactive Melt Infiltration

  • Received Date: 2007-12-26
  • Rev Recd Date: 2008-07-28
  • Available Online: 2025-07-28
  • Publish Date: 2009-02-15
  • C/C materials were prepared by liquid-vaporized and thermal-gradient CVI, and C/C-SiC composite with a density of 2.13~2.28 g/cm3 was prepared by reactive melt infiltration(RMI) in this paper. The microstructure of C/C-SiC was examined using XRD and OM, and its mechanical properties (flexural strength, compressive strength, hardness and fracture ductility), friction and wear characteristics were investi-gated. The results show that C/C-SiC is composed of C, SiC and Si. The lower the density of C/C, the higher the density of corresponding C/C-SiC. By graphitization, the flexural strength of C/C-SiC decreased from 203~275 MPa to150~210 MPa and the compressive strength decreased from463~607 MPa to 403~536 MPa, but the fracture ductility increased from 6.6~8.5 MPa·m1/2 to 7.3~9.2 MPa · m1/2. During the sliding friction of C/C-SiC disc to SiC pin, the friction coeffici~ent was about 0.19. By graphitization, the friction coefficient decreased to 0.14~0.15, but the average volume loss rate increased from 3.4×10-3~5.0×10-3mm3/h to 7.9×10-3~9.8×10-3mm3/h.

     

  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Article Metrics

    Article views (3) PDF downloads(0) Cited by()
    Proportional views
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return