ZHOU Bang-xin, YAO Mei-yi, MIAO Zhi, LI Qiang, LIU Wen-qing. Cracking Induced by Oxidation-Hydriding in Welding Joints of Zircaloy-4 Plates[J]. Nuclear Power Engineering, 2006, 27(1): 34-36.
Citation: ZHOU Bang-xin, YAO Mei-yi, MIAO Zhi, LI Qiang, LIU Wen-qing. Cracking Induced by Oxidation-Hydriding in Welding Joints of Zircaloy-4 Plates[J]. Nuclear Power Engineering, 2006, 27(1): 34-36.

Cracking Induced by Oxidation-Hydriding in Welding Joints of Zircaloy-4 Plates

  • Received Date: 2004-11-29
  • Rev Recd Date: 2005-03-27
  • Available Online: 2025-07-29
  • The welding joints of three plates of Zircaloy-4 obtained by hot rolling diffusion welding at 800℃ in vacuum were cracked during autoclave tests at 400℃ superheated steam after exposure longer than 150 days.The section of specimens was examined by optical microscopy and the composition of mi-cro-area at the welding seams and the matrix was analyzed and compared.The result shows that the con-tamination of carbon at the welding surface and the combination of oxidation and hydriding induced cracking is responsible for the cracking of welding seams during autoclave testing.

     

  • loading
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Article Metrics

    Article views (8) PDF downloads(0) Cited by()
    Proportional views
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return